第1页共21页编号：时间：2021年x月x日书山有路勤为径，学海无涯苦作舟页码：第1页共21页英制单位ENGLISHUNITS下列压力-温度表来自ANSIB16.34-1996版，包括行业内最常用的阀体和阀帽材料。Thefollowingpressure-temperaturechartsarederivedfromANSIB16.34-1996Version.Itwillcoverthemostcommonly-usedbodyandbonnetmaterialsintheIndustry.ASTMA216等级WCBASTMA216GR.WCB华氏度oF标准等级B16.34-1996STANDARDCLASSB16.34-1996特殊等级B16.34-1996SPECIALCLASSB16.34-1996最大非冲击工作压力，PSIGMAXIMUMNON-SHOCKWORKINGPRESSURE,PSIG最大非冲击工作压力，PSIGMAXIMUMNON-SHOCKWORKINGPRESSURE,PSIG1503006009001500250015030060090015002500流体静力学壳体检测HYDROSTATICSHELLTEST4501125222533505575927545011252250337556259375流体静力学密封检测HYDROSTATICSEATTEST32582516502450410068003258251650247541256875-20TO10020030028526023074067565514801350131522202025197037053375328061705625547029029029075075075015001500150022502250225037503750375062506250625040050060020017014063560055012701200109519001795164031702995273552804990456029029027575075071515001500142522502250214037503750356562506250594065070075012511095535535505107510651010161016001510268526652520447544404200270265240700695630140013901260210020801890349534703150582557805250800804108251235206034302005151030154525704285注意：在长时间处于温度超过426oC的环境中，碳钢的碳化物相可能转化为石墨。允许，但是建议不要长时间在温度超过426oC的环境中使用。NOTE:Uponprolongedexposuretotemperaturesabove800oF,thecarbidephaseofcarbonsteelmaybeconvertedtographite.Permissible,butnotrecommendedforprolongedusageabove800oF.第2页共21页第1页共21页编号：时间：2021年x月x日书山有路勤为径，学海无涯苦作舟页码：第2页共21页ASTMA216等级WCCASTMA216GR.WCC华氏度oF标准等级B16.34-1996STANDARDCLASSB16.34-1996特殊等级B16.34-1996SPECIALCLASSB16.34-1996最大非冲击工作压力，PSIGMAXIMUMNON-SHOCKWORKINGPRESSURE,PSIG最大非冲击工作压力，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注意：在长时间处于温度超过426oC的环境中，碳钢的碳化物相可能转化为石墨。允许，但是建议不要长时间在温度超过426oC的环境中使用。NOTE:Uponprolongedexposuretotemperaturesabove800oF,thecarbidephaseofcarbonsteelmaybeconvertedtographite.Permissible,butnotrecommendedforprolongedusageabove800oF.ASTMA352等级LCBASTMA352GR.LCB华氏度oF标准等级B16.34-1996STANDARDCLASSB16.34-1996特殊等级B16.34-1996SPECIALCLASSB16.34-1996最大非冲击工作压力，PSIGMAXIMUMNON-SHOCKWORKINGPRESSURE,PSIG最大非冲击工作压力，PSIGMAXIMUMNON-SHOCKWORKINGPRESSURE,PSIG1503006009001500250015030060090015002500第3页共21页...