Type NT(Normal Tensile) HT(High Tensile) Bicycle & Motorcycle 0.78, 0.95 Passenger Car 0.94, 0.95, 0.96, 1.20 HT 0.95, 1.20, 1.30, 1.39 Light Truck 1.20, 1.42 Truck & Bus 1.55, 1.65, 1.83 HT 1.60, 1.83 Tire Cross Section Structure (Left: Bias, Right: Radial) Type NT/ HT Diameter (mm) Breaking Force (Kg) Tensile Strength (Kg/mm2) Elonga tion (%) Torsion (Turns /100D) Adhesion (Kg/in2) Bronze Plating Weight (g/Kg) Sn (%) 0.94 NT 0.94± 0.02 Min. 130 Min. 180 Min. 4.0 Min. 25 Min. 60 0.488± 0.097 7± 3 0.95 NT 0.95± 0.02 Min. 130 Min. 180 Min. 4.0 Min. 27 Min. 60 0.475± 0.175 2± 1 10± 5 0.96 NT 0.96± 0.02 Min. 135 Min. 190 Min. 5.0 Min. 27 Min. 60 0.50± 0.20 13± 2 1.20 NT 1.20± 0.02 Min. 200 Min. 180 Min. 5.0 Min. 20 Min. 90 0.45± 0.15 11± 2 0.95 HT 0.95± 0.02 Min. 156 Min. 220 Min. 4.0 Min. 27 Min. 70 0.485± 0.095 7± 3 1.20 HT 1.20± 0.02 Min. 230 Min. 200 Min. 4.0 Min. 27 Min. 90 0.40± 0.15 7± 3 1.30 HT 1.30± 0.02 Min. 285 Min. 215 Min. 7.0 Min. 40 (/20cm) Min. 20 (/in0.5) 0.35± 0.20 Max1.5 1.39 HT 1.39± 0.03 Min. 300 Min. 200 Min. 5.0 Min. 20 Min. 87 0.35± 0.15 2± 1 Type NT/ HT Diameter (mm) Breaking Force (Kg) Tensile Strength (Kg/mm2) Elonga tion (%) Torsion (Turns /100D) Adhesion (Kg/in2) Bronze Plating Weight (g/Kg) Sn (%) 1.20 NT 1.20± 0.02 Min. 200 Min. 180 Min. 5.0 Min. 20 Min. 90 0.45± 0.15 11± 2 1.42 NT 1.42± 0.02 Min. 280 Min. 175 Min. 4.0 Min. 25 Min. 60 0.50± 0.20 7± 2 Type NT/ HT Diameter (mm) Breaking Force (Kg) Tensile Strength (Kg/mm2) Elonga tion (%) Torsion (Turns /100D) Adhesion (Kg/in2) Bronze Plating Weight (g/Kg) Sn (%) 1.55 NT 1.55±0.02 Min. 330 Min. 175 Min. 5.0 Min. 20 Min. 95 0.45± 0.15 11± 2 1.65...