火力发电厂常见金属材料硬度值范围全VIP专享

火力发电厂常见测试部件的硬度值范围部件名称序号材料牌号硬度值范围验收标准号火 电 厂常 用 钢材1 SA210C HB≤179 ASTM A210 2 SA234-WPC HB≤197 ASTM A234 3 SA234-WPB HB≤197 ASTM A234 4 20MnMo HB149～217 JB755 5 15MnMoV HB156～228 JB755 6 SA209T1 HB≤146 ASTM A209 7 SA182F1 HB143～192 ASTM A182 8 SA234-WP111类HB≤197 ASTM A234 9 SA234-WP121类HB≤197 ASTM A234 l0 T1 HB≤146 ASTM A209 11 A691-11/4Cr HB≤201 ASTM A691 l2 SA213-T2 HB≤217 ASTM A213l3 SA182-F2 HB143～192 ASTM A182l4 SA182-F12 HB 121～174 ASTM A182l5 T11 HB≤163 ASTM A213l6 T12 HB≤163 ASTM A213l7 T23 HB≤220 ASTM A213l8 SA182-F22 HB≤170 ASTM A182l9 1Cr5Mo HB 156～241 JB755 2O T9l HB≤250 ASTM A213 2l T92 HB≤250 ASTM A213 22 1Crl3 HB≤159 GB 1220 23 OCrl3A1 HB≤183 GB 1220 24 1Crl8Ni9 HB≤187 GB 1220 25 0Cr23Ni13 HB≤187 GB 1220 26 1Cr18Ni9Ti HB≤187 GB 1220 27 l0 HB≤137 GB3087 28 20 HB≤156 GB3087 29 12Cr2Mo HB≤170 GB5310 30 10CrMoV HB≤166 GB5310 3l 15CrMo HB≤179 GB5310 32 ZG20CrMo HB 135～140 DJ156 33 ZGZOCrMoV HB135～140 JB264O 34 ZG15Cr1Mo1V HB2OO～255 JB264O 直管、弯管、导汽管1 12Cr1MoV HB≤170 2 Cr2Mo1 HB≤170 3 SA213:T9 HB≤179 4 SA213:其他HB≤163 合 金 钢联箱1 12Cr1MoV HB≤170 2 10CrMo9lO HB≤170 焊缝同种钢焊接接头焊缝硬度热处理后一般不超过母材HB加100；异种港焊接接头的非奥氏体焊缝，其热处理后的硬度一般不超过高合金钢母材 HB加100; 两者同时须满足下列规定: l 合金总含量 <3% HB≤270 同种钢 : DL/T 869 一2012 异种钢 : DL/T 752 一2010 2 合金总含量 3%～10% HB≤300 3 合金总含量 >10% HB≤350 注: 异种钢以合金含量低侧母材的成分计算合金总含量汽 轮 机转子l 25Cr2Ni4MoV HB230～260 (236 ～286) 2 34CrNi3Mo HB240～270 3 30Cr2MoV(P2) HB255～321 (241 ～277) 4 30Cr1Mo1V HB250～280 JB/T 1265 高温螺栓l 35 HB146～187 DL439-91 2 45 HB187～227 3 20CrMo HB197～241 4 35CrMo HB217～255 5 20Cr1...