不锈钢化学成分对比表

部分不锈钢化学成分对比表 部分不锈钢化学成份表 规格 化学成份(%) 中国 C Si Mn P S Ni Cr Mo 0Cr19Ni9 ≤0.08 ≤1.00 ≤2.00 ≤0.035 ≤0.035 8.00-10.50 18.00-20.00 0Cr19Ni11 ≤0.030 ≤1.00 ≤2.00 ≤0.035 ≤0.035 9.00-13.00 18.00-20.00 0Cr17Ni12Mo2 ≤0.08 ≤1.00 ≤2.00 ≤0.035 ≤0.035 10.00-14.00 16.00-18.00 2.00-3.00 0Cr19Ni14Mo2 ≤0.030 ≤1.00 ≤2.00 ≤0.035 ≤0.035 12.00-15.00 16.00-18.00 2.00-3.00 日本 SUS304 ≤0.08 ≤1.00 ≤2.00 ≤0.040 ≤0.040 8.00-11.00 18.00-20.00 SUS304L ≤0.030 ≤1.00 ≤2.00 ≤0.040 ≤0.040 9.00-13.00 18.00-20.00 SUS316 ≤0.08 ≤1.00 ≤2.00 ≤0.040 ≤0.040 10.00-14.00 16.00-18.00 2.00-3.00 SUS316L ≤0.030 ≤1.00 ≤2.00 ≤0.040 ≤0.040 12.00-16.00 16.00-18.00 2.00-3.00 美国 Tp304 ≤0.08 ≤0.75 ≤2.00 ≤0.040 ≤0.040 8.00-11.00 18.00-20.00 Tp304L ≤0.035 ≤0.75 ≤2.00 ≤0.040 ≤0.040 8.00-13.00 18.00-20.00 Tp316 ≤0.08 ≤0.75 ≤2.00 ≤0.040 ≤0.040 11.00-14.00 16.00-18.00 2.00-3.00 Tp316L ≤0.035 ≤0.75 ≤2.00 ≤0.040 ≤0.040 10.00-15.00 16.00-18.00 2.00-3.0 常用不锈钢种化学成分及性能对照表 钢种Type 化学成分（%）Chemical Composition（%） 机械性能 Mechanical properties KS （JIS) ZPSS C Cr Ni Mo 其它Others 热处理条件Heat Treatment 屈服强度（N/mm2） Yield strength 抗拉强度 Tensile strength 延伸率（%） Elongation 硬度 Hardness HB HRB HV 奥氏体AUSTENITE 301 301 ≤0.15 16.0～18.0 6.00～8.00 - - S ≥205 ≥520 ≥40 ≤207 ≤95 ≤218 301L 301L ≤0.030 16.0～18.0 6.00～8.00 - N≤0.20 S ≥215 ≥550 ≥45 ≤187 ≤90 ≤200 304 304 ≤0.08 18.0～20.0 8.00～10.50 - - S ≥205 ≥520 ≥40 ≤187 ≤90 ≤200 304J1 304Cu 0.02～0.05 16.5～17.1 7.5～7.9 - Cu1.9～2.2 S ≥155 ≥450 ≥40 ≤187 ≤90 ≤200 304L 304L ≤0.030 18.0～20.0 9.00～13.00 - - S ≥175 ≥480 ≥40 ≤187 ≤90 ≤200 304N1 304N1 ≤0.08 18.0～20.0 7.00～10.50 - N0.10～0.25 S ≥275 ≥550...