电解法处理含镍废水的研究分析 化学工程与工艺专业

电解法处理含镍废水的研究摘要：含镍废水不仅造成镍金属的浪费，并且带来环境污染。本文通过配制硫酸镍溶液模拟含镍废水，采用电解法确定最佳阳极材料为钌涂层钛板，并研究了电解时间、电流强度和 Ni2+浓度等因素对 Ni2+的回收率的影响。实验结果表明：在电解时间 240 min，电流强度 15 A，Ni2+浓度 20 g/L，电解温度 50 oC，pH 值 6，搅拌速率 300 r/min 的条件下，Ni2+的回收率为 85.42 %，电流效率为 52.16 %。关键字：电解法；含镍废水；回收率；电流效率；Study on electrolytic treatment of nickel - containing wastewaterAbstract: Wastewater containing nickel not only causes waste of nickel metal, but also brings environmental pollution. In this paper, nickel sulfate solution was used to simulate nickel-containing wastewater. The best anode material was determined to be ruthenium-coated titanium plate by electrolytic method. The effects of electrolysis time, current intensity and nickel ion concentration on Ni 2+ recovery were studied. The experimental results show that the recovery rate of Ni2+ is 85.42 %，and efficiency is 52.16 % under the condition of 240 min electrolysis time, 15 A amperage, 20 g/L，Ni2+ concentration, 50 °C electrolysis temperature, 6 pH and stirring rate of 300 r/min.Key words: Electrolysis method; Nickel-containing wastewater; Recovery rate; Current efficiency;0 引言镍是一种似银白色且延展性良好的金属，由于其高度抗腐蚀性和抗腐蚀性[1]，被广泛用于电镀行业。含镍电镀废水能够对人体造成巨大的健康危害，电解法处理废水具有效果好、效率高[2]等优点，本文通过硫酸镍溶液模拟电镀废水，以不锈钢为阴极，钌涂层钛板为阳极，分析了电解时间、电流强度和 Ni2+浓度等因素对 Ni2+的回收率的影响，得到其最佳工艺条件。1 实验材料及方法1.1 实验仪器及试剂实验所用化学试剂包括：乙二胺四乙酸二钠（AR），硫酸镍（AR），醋酸钠（AR），二甲酚橙（AR），氢氧化钠（AR），盐酸（AR），硫酸（AR），锌粉（AR），冰醋酸（AR）等。实 验 所 用 仪 器 包 括 ： PHS-3C 型 pH 计 、FA...