奥氏体不锈钢的晶间腐蚀VIP专享

第 18 卷第 5 期腐蚀科学与防护技术Vol 18 No 52024 年 9 月CO RROSIO N SCIENCE AND PROTECTIO N TECHNOLO GYSep 20241 11奥氏体不锈钢的晶间腐蚀罗 宏,龚 敏理工学院材料与化学工程系,643000摘要:主要介绍了奥氏体不锈钢晶间腐蚀的机理。讨论了 C、Cr、P 等元素以与冷加工、铸造、焊接、热作成型等热加工方法对晶间腐蚀的影响;降低奥氏体不锈钢晶间腐蚀敏感性主要是限制不锈钢中的 C 和 N 的含量分别不超过0103 %和 0110 %的和进行固溶处理.关键词:奥氏体不锈钢;晶间腐蚀;综述中图分类号 : T G157 文献标识码 :A 文章编号:100226495 (2024) 0520357204O N INTERGRANUL AR CO RROSIO N OF AUSTENITIC STAINL ESS STEELL UO Ho ng , GON G MinM ateri al an d Chem ical Engi neeri ng Depart ment , S ichuan U ni versty of S cience an d Engi neeri ng , Zigong 643000ABSTRACT :The mechanisms of intergranular co rro sio n ( I GC) of austenitic stainless steel were int roduced. The effect s of co ntent of carbo n ,chro mium and nit rogen etc. as well as of cool wo rk ,casting ,12welding etc. o n I GC were discussed fo r austenitic stainless steel . In o rder to mitigating t he suscep tibility to I GC , t he co ntent of carbo n and nit rogen sho uld be limited to 0 . 03 % ( maximum)and 0 . 10 %( maximum)respectively ,o n t he ot her hand ,a p roper solutio n heat t reating sho uld also be taken.KEY WO RDS :austenitic stainless steel ;intergranular co rro sio n ; review晶间腐蚀( I GC) 是一种常见的局部腐蚀 ,遭受这种腐蚀C 处于过饱和 ,受到敏化处理时 , C 和 Cr 形成碳化物 (主要的不锈钢 ,表面看来还很光亮 ,但经不起轻轻敲击便会破裂为(Cr , Fe)23C6 型) 在晶界析出. 由于( Cr , Fe)23C6 含 Cr 量很成细粒. 由于晶间腐蚀不易检查 ,造成设备的突然破坏 ,所以高 ,而 Cr 在奥氏体中扩散速率很低 ,这样就在晶界两侧形成危害性极大[ 1 ],统计资料认为这类腐蚀约占总腐蚀类型的了贫 Cr 区 ,其含 Cr 量低于 12mass % ,...