电熔锆刚玉砖的生产工艺VIP免费

1玻璃窑用电熔锆刚玉砖的熔铸工艺路玉超摘要近年来，我国熔铸耐火材料熔铸工艺方面有了很大发展，详细介绍了AZS锆刚玉砖从原料、制模到浇铸以及浇铸后退火的全过程，着重讲述了熔融工艺、浇铸工艺以及浇铸过程中产生的缺陷和防治方法。关键词：AZS高刚玉砖砂型熔融工艺浇铸工艺缺陷冒口2目录一熔化工艺.........................................................31.AZS原料......................................................32．电弧炉工作原理...............................................33．AZS熔化原理..................................................33.1熔化过程的物理化学反应...................................34.熔融工艺.....................................................54.1还原法...................................................54.2氧化法...................................................5二．砂型的制作......................................................61.砂型制备的原料...............................................61.1有较好的透气性...........................................61.2有良好的耐热冲击强度.....................................61.3有良好的热机械性能.......................................61.4锆刚玉砖表面不产生化学粘砂...............................62.砂型的制作工艺...............................................6三.浇铸.............................................................71.浇铸的方法...................................................71.1普通浇铸法...............................................71.2倾斜浇铸法...............................................71.3无缩孔浇铸...............................................72.浇铸过程的特征...............................................73.浇铸工艺.....................................................83.1浇铸温度.................................................83.2浇铸速度和浇铸时间.......................................83.3补浇.....................................................94.浇铸与浇铸中气孔的关系.......................................94.1由铸型材料引发的气孔.....................................94.2由浇铸操作引发的气孔.....................................95.浇铸过程中的缺陷及防治措施..................................105.1浇铸过程中的缺陷........................................105.2铸件中缩松的形成及其影响因素............................115.3减少铸件缩松和缩孔的基本方法............................115.4冒口....................................................11四.AZS退火工艺....................................................121.铸件的凝固..................................................122.铸件的退火..................................................132.1保温箱退火法............................................132.2隧道窑退火..............................................13结论...............................................................14参考文献...........................................................143玻璃窑用锆刚玉砖的熔铸工艺一熔化工艺1.AZS原料AZS用原料有五种：氧化铝、锆英砂、富锆砂、纯碱、硼砂。1)氧化铝的引入一般选用工业氧化铝，生产要求其含水量应小于0.3%，烧失量最好小于0.15%，一吨AZS-33电熔砖约需0.62吨氧化铝。2)锆英砂主要引入2ZrO和2SiO,但其中还含有少量的2TiO和23FeO，23FeO能使AZS产品染色，造成粗晶砂眼，同时也影响开裂，故其含量应小于0.2%,2TiO影响铸件在冷却过程中开裂，另外也会影响产品的氧化工艺，故其含量应限制小于0.2%，吨AZS-33电熔砖约需0.65锆英砂。3)富锆砂又称脱硅锆，AZS中的二氧化硅全部来源于锆英石，2ZrO不足部分，由富锆砂...