机械类英文文献+翻译VIP免费

机械工业出版社2004年3月第1版20.9MACHINABILITYThemachinabilityofamaterialusuallydefinedintermsoffourfactors:1、Surfacefinishandintegrityofthemachinedpart;2、Toollifeobtained;3、Forceandpowerrequirements;4、Chipcontrol.Thus,goodmachinabilitygoodsurfacefinishandintegrity,longtoollife,andlowforceAndpowerrequirements.Asforchipcontrol,longandthin(stringy)curedchips,ifnotbrokenup,canseverelyinterferewiththecuttingoperationbybecomingentangledinthecuttingzone.Becauseofthecomplexnatureofcuttingoperations,itisdifficulttoestablishrelationshipsthatquantitativelydefinethemachinabilityofamaterial.Inmanufacturingplants,toollifeandsurfaceroughnessaregenerallyconsideredtobethemostimportantfactorsinmachinability.Althoughnotusedmuchanymore,approximatemachinabilityratingsareavailableintheexamplebelow.20.9.1MachinabilityOfSteelsBecausesteelsareamongthemostimportantengineeringmaterials(asnotedinChapter5),theirmachinabilityhasbeenstudiedextensively.Themachinabilityofsteelshasbeenmainlyimprovedbyaddingleadandsulfurtoobtainso-calledfree-machiningsteels.ResulfurizedandRephosphorizedsteels.Sulfurinsteelsformsmanganesesulfideinclusions(second-phaseparticles),whichactasstressraisersintheprimaryshearzone.Asaresult,thechipsproducedbreakupeasilyandaresmall;thisimprovesmachinability.Thesize,shape,distribution,andconcentrationoftheseinclusionssignificantlyinfluencemachinability.Elementssuchastelluriumandselenium,whicharebothchemicallysimilartosulfur,actasinclusionmodifiersinresulfurizedsteels.Phosphorusinsteelshastwomajoreffects.Itstrengthenstheferrite,causingincreasedhardness.Hardersteelsresultinbetterchipformationandsurfacefinish.Notethatsoftsteelscanbedifficulttomachine,withbuilt-upedgeformationandpoorsurfacefinish.Thesecondeffectisthatincreasedhardnesscausestheformationofshortchipsinsteadofcontinuousstringyones,therebyimprovingmachinability.LeadedSteels.Ahighpercentageofleadinsteelssolidifiesatthetipofmanganesesulfideinclusions.Innon-resulfurizedgradesofsteel,leadtakestheformofdispersedfineparticles.Leadisinsolubleiniron,copper,andaluminumandtheiralloys.Becauseofitslowshearstrength,therefore,leadactsasasolidlubricant(Section32.11)andissmearedoverthetool-chipinterfaceduringcutting.Thisbehaviorhasbeenverifiedbythepresenceofhighconcentrationsofleadonthetool-sidefaceofchipswhenmachiningleadedsteels.Whenthetemperatureissufficientlyhigh-forinstance,athighcuttingspeedsandfeeds(Section20.6)—theleadmeltsdirectlyinfrontofthetool,actingasaliquidlubricant.Inadditiontothiseffect,leadlowerstheshearstressintheprimaryshearzone,reducingcuttingforcesandpowerconsumption.Leadcanbeusedineverygradeofsteel,suchas10xx,11xx,12xx,41xx,etc.LeadedsteelsareidentifiedbytheletterLbetweenthesecondandthirdnumerals(forexample,10L45).(Notethatinstainlesssteels,similaruseoftheletterLmeans“lowcarbon,”aconditionthatimprovestheircorrosionresistance.)However,becauseleadisawell-knowntoxinandapollutant,thereareseriousenvironmentalconcernsaboutitsuseinsteels(estimatedat4500tonsofleadconsumptioneveryyearintheproductionofsteels).Consequently,thereisacontinuingtrendtowardeliminatingtheuseofleadinsteels(lead-freesteels).Bismuthandtinarenowbeinginvestigatedaspossiblesubstitutesforleadinsteels.Calcium-DeoxidizedSteels.Animportantdevelopmentiscalcium-deoxidizedsteels,inwhichoxideflakesofcalciumsilicates(CaSo)areformed.Theseflakes,inturn,reducethe...