NiZn铁氧体材料特性NiZn Ferrite material Characteristics材质初始磁导率μi比温度系数αμir居里温度Tc密度d电阻率ρInitialRelative temperature Curie ElectricPermeabilityfactor of μiTemperatureresistivity/mTKA/m×10-6MHz×10-6/℃℃g/cm3Ω-mTN4N40±25%2804.0≤3002050>3004.810 6TN12B120±20%4304.0≤650.122>2305.010 6TN20H200±20%4304.0≤450.145>3005.010 6TN20B200±20%5008.0≤500.125>3005.210 6TN25B250±20%4754.0≤400.124>3005.210 6TN25H250±20%4204.0≤300.530>3005.010 6TN25Y250±20%4004.0≤500.130>2205.010 6TN30H300±20%4154.0≤300.120>2605.010 6TN35B350±20%4604.0≤350.125>2605.210 6TN35H350±20%4504.0≤250.120>2605.210 6TN40H400±20%4104.0≤250.1252505.010 6TN41H400±20%4304.0≤250.18>2305.110 6TN40L400±20%4404.0≤200.117>2305.010 6TN40S400±20%4604.0≤250.125>2305.2510 6TN45B450±20%4404.0≤250.115>2605.010 6TN39H500±20%4104.0≤250.113>1905.110 6TN65B650±20%4004.0≤170.118>1905.010 6TN65H650±20%4004.0≤150.18>1855.010 6TN65G625±20%2704.0160.18>1705.010 6TN80L800±25%4104.0≤130.19>1905.010 6TN80G800±20%2704.0≤300.115>1204.910 5TN90H900±20%3404.0≤200.115>1405.010 6TN100B1000±20%3204.0≤100.055>1305.010 6TN120L1200±20%3601.6≤180.1/>1605.010 6TN140L1400±20%3501.6≤180.1/>1455.010 6TN150P1500±20%2800.8≤200.15>1055.010 6TN160L1600±20%3301.6≤180.1/>1355.010 6TN200B2000±20%2904.0≤100.015>1005.010 6注:通常特性指标的测试温度为25℃,特别标注除外。Note. All the character is tested at 25℃ except the marked ones.MaterialFlux densityRelative loss factor NiZn材料特性表与特性曲线 Material Characteristic Sheet ﹠ Figu resDensity饱和磁感应强度Bs 相对损耗因子tanδ/μi材料/Material:TN4N特点/Features:1. 高频率材料/High Frequency MaterialInitial permeabilityμi25℃40±25%Saturation magneticBs(mT)flux density4000A/mRelative loss factor20MHzRelative temperaturecoefficientCurie temperatureTc(℃)>300Electrial resistivityρ(Ω·m)10 6Densityd(kg/m3)4.8× 103Test core:Toroid(mm) OD: 12.7 ID: 7...