激光重熔对 50CrMoV 钢放电强化外表组织与性能的影响乔桂英 肖福仁摘 要:用透射电镜和 X-射线衍射讨论了激光重熔对 50CrMoV 钢脉冲放电强化层组织与性能的影响,结果说明:激光重熔可使放电外表强化层的硬度进一步提高。硬度提高的原因是激光超细化组织及高密度位错和一定量的碳化物所致。关键词:激光重熔 放电强化 组织 硬度Effect of Laser Cladding on Microstructureand Property of Pulse Discharge EnhancedSurface Layer of Steel 50CrMoVQiao Guiying and Xiao Furen(Material and Chemistry Institute, Yanshan University, Qinhuangdao 066004)Abstract:The effect of laser cladding on microstructure and property of pulse discharge enhanced surface layer of steel 50CrMoV has been studied by means of transmission electron microscope and x-ray diffraction method. The results showed that the hardness of pulse discharge enhanced layer was improved by laser cladding to form nanometer crystal microstructure, higher density dislocation and definite carbides.Material Index:Laser Cladding, Discharge Enhancing, Microstructure, Hardness▲ 放电强化作为一种外表强化的手段得到一定的作用[1,2],然而放电强化层较薄,强化层的均匀性和致密性较差,因此影响了其强化的效果。随大功率激光器的出现,激光外表处理在工业生产取得广泛的应用[3]。近年来,有关激光熔覆 WC/Co(Ni)和 TiC/Ni(Co)合金的讨论较多[4,5],广泛采纳的是人工或机械涂刷粉末的方法。本工作采纳脉冲放电的方法,在 50CrMoV 钢外表预涂一层硬质合金硬化层,讨论激光重熔对脉冲放电强化层的影响,以进一步提高脉冲放电外表强化性能。1 试验材料及方法 基体材料选用 50CrMoV 钢。在基体材料外表采纳脉冲放电的方法形成 20μm 左右厚的预涂层,然后进行激光处理。脉冲放电试验在自行研制的晶体脉冲电源加管旋转电极强化试验机上进行,采纳 YG8 合金为电极材料,工作条件为:占空比为 9:1;电压为 180V;强化时间为 8min/cm2;介质为空气。激光处理在 2kW 连续 CO2激光器上进行。束斑直径D=5mm;功率 P=600~1 500W;扫描速度 v=10~25mm/s;N2保护。 在 D/MAX-rB 型 X 射线衍射仪上进行物相分析。在...

1、当您付费下载文档后,您只拥有了使用权限,并不意味着购买了版权,文档只能用于自身使用,不得用于其他商业用途(如 [转卖]进行直接盈利或[编辑后售卖]进行间接盈利)。
2、本站所有内容均由合作方或网友上传,本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺!文档内容仅供研究参考,付费前请自行鉴别。
3、如文档内容存在违规,或者侵犯商业秘密、侵犯著作权等,请点击“违规举报”。

碎片内容

激光重熔对50CrMoV钢放电强化表面组织与性能的影响

确认删除?
VIP
微信客服
  • 扫码咨询
会员Q群
  • 会员专属群点击这里加入QQ群
客服邮箱
回到顶部