LaboratoryTestFrequencyFormandOtherRegularForms试验室检测频率以及常用表格试验项目TestContent检测频率TestFrequency1.原材料RawMaterials水泥品质QualityofCement200~400T/1(次time)细骨料品质QualityofFineAggregates600T~1200T/1(次time)粗骨料品质QualityofCoarseAggregates1000T~2000T/1(次time)外加剂Additives减水Water-reducingAgent50T/1(次time)引气剂Air-entrainingAgent2T/1(次time)速凝剂Accelerator100T/1(次time)钢筋Rebar60T/1(次)2.拌合楼BatchingPlant衡量误差MeasurementError4h/1(次time)拌合时间BatchingTime4h/1(次time)计量器具效验CheckingofMeasuringInstruments月Month/1(次time)砂石含水量WaterContentofSandsandStones班Shift/2(次time)(或要求orasrequired)砂细度模数FinenessModulusofSands天Day/1(次time)砂含泥(粉)量Silt(Powder)ContentofSands天Day/1(次time)粗骨料超逊径、含泥(粉)Over-sizeandUnder-sizeCoarseAggregatesandSilt(Powder)Content班Shift/1(次time)3.混凝土拌合物ConcreteMixture坍落度Slump4h/1(次time)含气量AirEntrainment4h/1(次time)温度Temperature4h/1(次time)4.混凝土性能指标ConcreteDurabilityIndex强度Strength大体积BulkVolume500M31(组Group)非大体积Non-bulkVolume100M3/1(组Group)抗渗Seepage-resistant季度Season/1(次time)抗冻Frost-resistant季度Season/1次time)极拉UltimateTensile季度/Season1(次time)执行标准ReferredStandards:DL/T5144-2001砂细度模数试验报告SandFinenessModulusTestReport试样产地SampleLocation:取样日期SampleDate:矚慫润厲钐瘗睞枥庑赖。试验编号TestNo.检测地点Checkingplace:聞創沟燴鐺險爱氇谴净。颗粒成份ParticleConstituent试验日期TestDate:残骛楼諍锩瀨濟溆塹籟。MeshsizeWt.ofRetained(g)Cumulativewt.ofRetained(g)CumulativePercentRetainedCumulativePercentofPassingRemarksmmNo.9.53/8/4.754/2.368/1.1816/0.630/0.350/0.15100/0.075200/筛出Screened/FM=共计Sumtotal/QualitySpecified:F.M≥2.3and≤3.1散失Dispersed/Conclusion:□Acceptance□Notacceptance2.筛分曲线ScreenCurveTestedby试验人员:calculatedby:计算Checkedby校核:酽锕极額閉镇桧猪訣锥。砼极限拉伸试验记录ULTIMATETENSILECAPACITYOFCONCRETEPROJECTNAME:记录号FormNo.:工程部位Location设计标号DesignedGrade(QualitySpecified)混凝土种类Concretetype试件编号SampleNo.配合比编号MixingProportionN0.成型日期CastDate检测日期TestDate龄期Age(days)试件尺寸SampleSizeSpecimenNumber第一块No.1第二块No.2第三块No.3第四块No.4荷载Load(KN)应力stress(MPa)左Left右Right平均Average左Left右Right平均Average左Left右Right平均Average左Left右Right平均Average00///20.2///40.4///60.6///80.8101121.2141.4161.6181.8202222.2极限荷载LimitLoad(KN)/tensilestrength(MPa)/Averagetensilestrength(MPa)Ultimatetensilecapacity(1×10-6)Averageultimatetensilecapacity(1×10-6)Testedby试验人员:calculatedby:计算Checkedby审检:彈贸摄尔霁毙攬砖卤庑。水泥物理性能检测报告PhysicalTestingReportofCement(DL/T5144-2001)PROJECTNAME:记录号FormNo.:使用编号useNo.:试验编号TestingNo.生产厂家Manufacturer品种及标号Type检测依据TestingReference检测地点TestingLocationlaboratory检测日期TestingDate取样地点SamplingPlace取样日期SamplingData检测设备名称InstrumentCementmortarmixerCementSettingtimemeter&consistencymeterCementsuctionsievinganalyzer细度Finesse标准稠度SpecifiedConsistency安定性AutoclaveExpension烘干样重WeightofDriedSample(g)筛余量WeightofScreenResidue(g)筛余百分比PercentageofScreenResidue%平均Average%试样重SampleWeight(g)需水量WaterConsumption(ml)%平均Average%Acceptance凝结时间SettingTime(min)比重SpecificGravity12平均Average试样重SampleWeight(g)初始刻度InitialSettingCalibrati...