临钢目前所炼钢种化学成分要求 Q 195～Q 295 钢种化学成分 钢种 标准 C% Si% Mn% P% S% Q195 GB/T700-2006 ≤0.12 ≤0.30 ≤0.50 ≤0.035 ≤0.040 内控 0.08～0.10 0.13～0.18 0.40～0.50 ≤0.035 ≤0.040 Q215A GB/T700-2006 ≤0.15 ≤0.35 ≤1.20 ≤0.045 ≤0.050 内控 0.10～0.13 0.13～0.18 0.40～0.55 ≤0.045 ≤0.050 Q215B GB/T700-2006 ≤0.15 ≤0.35 ≤1.20 ≤0.045 ≤0.045 内控 0.10～0.13 0.13～0.18 0.40～0.55 ≤0.045 ≤0.045 Q235A GB/T700-2006 ≤0.22 ≤0.35 ≤1.40 ≤0.045 ≤0.050 内控 0.14～0.18 0.13～0.18 0.45～0.60 ≤0.045 ≤0.050 Q275A GB/T700-2006 ≤0.24 ≤0.35 ≤1.50 ≤0.045 ≤0.050 内控 0.16～0.22 0.13～0.18 0.65～0.75 ≤0.045 ≤0.050 Q275B GB/T700-2006 厚度≤40mm ≤0.21 ≤0.35 ≤1.50 ≤0.045 ≤0.045 GB/T700-2006 厚度＞40mm ≤0.22 ≤0.35 ≤1.50 ≤0.045 ≤0.045 内控 0.15～0.20 0.13～0.18 0.65～0.75 ≤0.045 ≤0.045 Q295A GB/T1591-94 ≤0.16 ≤0.55 0.80～1.50 ≤0.045 ≤0.045 内控 0.10～0.15 0.20～0.40 1.00～1.30 ≤0.035 ≤0.040 Q235B 钢种化学成分 标准 C% Si% Mn% P% S% GB/T700-2006 ≤0.20 ≤0.35 ≤1.40 ≤0.045 ≤0.045 Q235B1内控 0.13～0.20 0.16±0.01 0.12～0.30 0.43±0.03 ≤0.030 ≤0.030 Q235B2内控 0.06～0.14 0.10±0.01 0.12～0.30 0.43±0.03 ≤0.030 ≤0.030 Q235C 钢种化学成分 项 目 C% Si% Mn% P% S% GB/T700-2006 ≤0.17 ≤0.35 ≤1.40 ≤0.040 ≤0.040 冶炼内控 0.10～0.14 0.15～0.30 0.45～0.60 ≤0.025 ≤0.025 成品内控 0.11～0.16 0.15～0.30 0.45～0.60 ≤0.025 ≤0.015 Q235q C Q235q D 钢种化学成分 牌号 要求 化学成分 （％） C Si Mn P S AlS Q235q C 国标 ≤0.20 ≤0.30 0.40～0.70 ≤0.035 ≤0.035 冶炼内控 0.10～0.13 0.12～0.24 0.45～0.55 ≤0.025 ≤0.025 精炼内控 0.12～0.17 0.12～0.24 0.45～0.60 ≤0.025 ≤0.015 Q235q D 国标 ≤0.18 ≤0.30 0.50～0.80 ≤0.025 ≤0.025 ≥0.015 冶炼内控 0.11～0.13 0.20～0.40 1.20～1.40 ≤0.020 ≤0.025 精炼内控 0.12～0.16 0.12～0.24 0.55～0.70 ≤0.020...