二氧化钛光催化还原cr研究VIP专享

二氧化钛光催化还原 Cr（VI）讨论摘要：本文采纳溶胶－凝胶法（sol-gel）合成了纳米二氧化钛，在不同的焙烧条件下，获得了具有不同催化效果的二氧化钛光催化剂。采纳 XRD、UV-Vis 漫反射、静态吸附等手段对其进行了表征。对 Cr(VI)光催化还原的讨论结果表明：不同温度下焙烧的二氧化钛其光催化降解 Cr(VI)有很大差别，300oC 和 400oC 下焙烧的二氧化钛对 Cr(VI)有较高的去除效率，其效果明显优于其它温度下焙烧的二氧化钛。造成催化剂不同催化活性的原因主要是催化剂对 Cr(VI)的吸附能力和催化剂中锐钛矿含量的差异。关键词：二氧化钛；光催化；Cr(VI)还原On photo-reduction of Cr(VI) using TiO2 PhotocatalystAbstract: In this study, TiO2 photocatalysts with different properties were obtained through calcining titania prepared using sol-gel method at different temperatures. These photocatalytic materials were characterized using XRD, UV-Vis and static adsorption. The experimental results showed that different catalysts show different photocatalytic behaviors. The photocatalytic activity of titania calcined at 300oC and 400oC was significantly higher than those calcined at higher calcination temperatures, which is ascribed to the difference of Cr(VI) adsorption capacity and anatase content of the photocatalysts.Keywords: titania; photocatalysis; Cr(VI) photo-reduction1 引言 环境中的铬污染主要来自电镀、冶炼、制革、颜料和铬盐等工业生产过程中排出的废水、废渣等。以金属铬生产过程为例，在用水浸出可溶性的铬酸钠过程中会排出含 Cr(VI)的废水，废水中Cr(VI)浓度高达 30~144mg/L，排放量约 76m3/d[1]。废水中的 Cr(VI)会影响人体健康，讨论结果表明：Cr(VI)会造成对皮肤的刺激和对呼吸系统的损坏，1932 年，德国流行病学家 Grob 与 Kosch 提出吸入过量铬酸盐与肺癌有直接关联性[2]。因此，治理含 Cr(VI)废水对保护人体健康具有重要意义。目前，国内外常用的处理 Cr(VI)的方法主要有：化学沉淀法、离子交换法、活性炭吸附法等，其中化学沉淀法是常用的方法，但该法具有操作麻烦和成本高的问题，而离子交换法和吸附法只是从废水中分离出 Cr(VI)，其中 Cr(VI)并...